Composite Geomembrane Liner is made by heat-bonding nonwoven or woven geotextile combined with HDPE geomembranes by calendaring processing technology. composite geomembrane liner is automatically formed by pressing one or two geotextile layer to the geomembrane layer in the continuous far infrared ray heating oven, polymer and anti-aging materials are added in the production process at the same time, so it can be used in unconventional temperature environment.
The composite geomembrane liner provides the advantages of both geotextiles and geomembranes. The geotextile layer increases essential tensile strength and the geomembranes provides excellent impermeable, leak, moisture proof and tear and puncture resistance. Our composite geomembrane liner are widely used for landfills, waste water treatment, roads construction, aquaculture, landscape and agriculture, etc.
Composite Geomembrane Liner Specification
| Test Item | Test Properties | Unit | JC | JC5 | JC6 | JC7 | JC8 |
| Weight | g/m2 | 400 | 500 | 600 | 700 | 800 | |
| Film Thickness | mm | 0.25-0.35 | 0.30-0.50 | ||||
| Mechanical Properties | Break Strength | kN/m | 5.0 | 7.5 | 10 | 12 | 14 |
| Break Elongation | % | 30-100 | 30-100 | 30-100 | 30-100 | 30-100 | |
| CBR Burst Strength | KN | 1.1 | 1.5 | 1.9 | 2.2 | 2.5 | |
| Tear Resistance | KN | 0.15 | 0.25 | 0.32 | 0.4 | 0.48 | |
| Peel Strength | N/cm | ≥6 | ≥6 | ≥6 | ≥6 | ≥6 | |
| Hydrostatic Pressure | Film Thickness | mm | 0.2 | 0.3 | 0.4 | 0.5 | 0.6 |
| One cloth one film | MPa | 0.4 | 0.5 | 0.6 | 0.8 | 1 | |
| Two cloth one film | MPa | 0.5 | 0.6 | 0.8 | 1 | 1.2 |
High tensile strength.
Excellent chemical resistance.
Effective drainage and waterproof performance.
Excellent impermeable, leak and moisture proof.
Excellent UV resistance.
Excellent tear and puncture resistance.
Stable low temperature embrittlement resistance.
Easy to deploy.
Cost saving.
Anti-aging and anti-corrosion.
Composite Geomembrane Liner is made by heat-bonding nonwoven or woven geotextile combined with HDPE geomembranes by calendaring processing technology. composite geomembrane liner is automatically formed by pressing one or two geotextile layer to the geomembrane layer in the continuous far infrared ray heating oven, polymer and anti-aging materials are added in the production process at the same time, so it can be used in unconventional temperature environment.
The composite geomembrane liner provides the advantages of both geotextiles and geomembranes. The geotextile layer increases essential tensile strength and the geomembranes provides excellent impermeable, leak, moisture proof and tear and puncture resistance. Our composite geomembrane liner are widely used for landfills, waste water treatment, roads construction, aquaculture, landscape and agriculture, etc.
Composite Geomembrane Liner Specification
| Test Item | Test Properties | Unit | JC | JC5 | JC6 | JC7 | JC8 |
| Weight | g/m2 | 400 | 500 | 600 | 700 | 800 | |
| Film Thickness | mm | 0.25-0.35 | 0.30-0.50 | ||||
| Mechanical Properties | Break Strength | kN/m | 5.0 | 7.5 | 10 | 12 | 14 |
| Break Elongation | % | 30-100 | 30-100 | 30-100 | 30-100 | 30-100 | |
| CBR Burst Strength | KN | 1.1 | 1.5 | 1.9 | 2.2 | 2.5 | |
| Tear Resistance | KN | 0.15 | 0.25 | 0.32 | 0.4 | 0.48 | |
| Peel Strength | N/cm | ≥6 | ≥6 | ≥6 | ≥6 | ≥6 | |
| Hydrostatic Pressure | Film Thickness | mm | 0.2 | 0.3 | 0.4 | 0.5 | 0.6 |
| One cloth one film | MPa | 0.4 | 0.5 | 0.6 | 0.8 | 1 | |
| Two cloth one film | MPa | 0.5 | 0.6 | 0.8 | 1 | 1.2 |
High tensile strength.
Excellent chemical resistance.
Effective drainage and waterproof performance.
Excellent impermeable, leak and moisture proof.
Excellent UV resistance.
Excellent tear and puncture resistance.
Stable low temperature embrittlement resistance.
Easy to deploy.
Cost saving.
Anti-aging and anti-corrosion.